牌号
|
E460R低合金结构钢热轧钢板
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
中国ISC
|
L04604
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
对应标准
|
GB /T 3274-2017
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
碳素结构钢和低合金结构钢热轧钢板和钢带
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Hot-rolled plates, sheets and strips of carbon structural steels and high strength low alloy structural sheets
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
品牌/供货源
|
中国大陆-> 宝钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
归类
|
合金钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
强度 焊接性
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
标签
|
热轧钢板和钢带 低合金结构钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
说明
|
性能特点
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
与Q420相比，Q460D钢的强度更高，经正火、正火加回火或淬火加回火处理后有很高的综合力学性能，Q460D钢具有良好的韧性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
用途举例
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
属于备用钢种。主要用于各种大型工程结构及要求强度高、载荷大的轻型结构。广泛用于各类工程机械、如矿山和各类工程施工用的钻机、电铲、电动反斗车、矿用汽车、挖掘机、装载机、推土机、各类起重机、煤矿液压支架等机械设备及其他结构件。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
本标准适用于厚度不大于400mm的碳素结构钢和低合金钢热轧钢板和钢带
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
E460R 化学元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
N
|
Ti
|
V
|
Nb
|
B
|
Al b
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.015
|
|
最大值
|
0.2
|
0.6
|
1.8
|
0.03
|
0.025
|
0.3
|
0.8
|
0.55
|
0.2
|
0.015
|
0.2
|
0.2
|
0.11
|
0.004
|
-
|
|
钢的牌号和化学成分(熔炼分析)应符合GB/T 700和GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
b当采用全铝（Alt）含量表示时，Alt应不小于0.02%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
E460R 机械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
厚度（直径，边长）
|
抗拉强度
|
屈服点
|
断后伸长率或延伸率
|
|
|
|
|
|
|
|
|
|
|
|
|
|
t
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
|
|
|
|
|
|
|
mm
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
t≤16
|
550~720
|
≥460
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
|
|
16
|
550~720
|
≥440
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
|
|
40＜t≤63
|
550~720
|
≥420
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
63＜t≤100
|
550~720
|
≥400
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
100＜t≤150
|
530~700
|
≥380
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1、力学性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
①厚度小于3mm的钢板和钢带的抗拉强度和断后伸长率应符合GB/T 700、GB/T 1591的规定，断后伸长率允许比GB/T 700或GB/T 1591的规定降低5%(绝对值)。根据需方要求，钢板和钢带的屈服强度可按GB/T 700、GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
②厚度不小于3mm的钢板和钢带的力学和工艺性能应符合GB/T 700、GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2、工艺性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
钢板和钢带应做180°弯曲试验，试样弯曲压头直径应符合GB/T 700、GB/T 1591的规定。如供方能保证冷弯试验合格，可不作检验。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|