Grade :
|
Z3CND19-15-04压力用焊接钢管。不锈钢管
|
|
|
|
|
|
|
|
|
Number:
|
X2CrNiMo18-15-4
|
|
|
|
|
|
|
|
|
Classification:
|
奥氏体不锈钢-特殊等级
|
|
|
|
|
|
|
|
|
Density:
|
8 g/cm ³
|
|
|
|
|
|
|
|
|
Standard:
|
|
|
|
|
|
|
|
|
|
EN 10088-2:2005不锈钢。通用耐腐蚀钢片/板和带材交货技术条件
|
|
|
|
|
|
|
|
|
EN 10088-3:2005不锈钢。一般用途耐腐蚀钢的半成品、棒材、线材、型材和光亮产品的交货技术条件
|
|
|
|
|
|
|
|
|
EN 10028-7:2007压力用钢制扁平产品。不锈钢
|
|
|
|
|
|
|
|
|
EN 10217-7:2005压力用焊接钢管。不锈钢管
|
|
|
|
|
|
|
|
|
EN 10253-3:2008对焊管件。无特殊检验要求的锻造奥氏体和奥氏体-铁素体（双相）不锈钢
|
|
|
|
|
|
|
|
|
EN 10253-4:2008对焊管件。有特殊检验要求的锻制奥氏体和奥氏体-铁素体（双相）不锈钢
|
|
|
|
|
|
|
|
|
EN 10088-1:2005不锈钢。不锈钢清单
|
|
|
|
|
|
|
|
|
EN 10088-5:2009不锈钢。建筑用耐腐蚀钢棒材、棒材、线材、型材和光亮产品的交货技术条件
|
|
|
|
|
|
|
|
|
EN 10088-4:2009不锈钢。建筑用耐腐蚀钢片/板和带材交货技术条件
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Equivalent grades:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical comb % of steel X2CrNiMo18-15-4 (Z3CND19-15-04 ): EN 10088-2-2005
|
|
|
|
|
|
|
|
|
|
硫含量的特定范围可以提供特定性能的改善。对于可加工性，建议并允许将硫含量控制在0.015%至0.030%之间。对于可焊性，建议并允许将硫含量控制在0.008%至0.030%之间。对于可极化性，建议将硫含量控制在最大0.015%。
|
|
|
|
|
|
|
|
|
|
未经买方同意，不得故意将本表中未列出的元素添加到钢材中，除非对铸件进行精加工。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
Ni
|
P
|
S
|
Cr
|
Mo
|
N
|
|
max 0.03
|
max 1
|
max 2
|
13 - 16
|
max 0.045
|
max 0.015
|
17.5 - 19.5
|
3月4日
|
max 0.11
|
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X2CrNiMo18-15-4 (Z3CND19-15-04 )
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
500-720
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+AT)
|
490-690
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
200-240
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+AT)
|
220
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) transverse, (+A)
|
+20°
|
-196°
|
|
|
|
|
|
|
|
60
|
60
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) longitud., (+A)
|
+20°
|
|
|
|
|
|
|
|
|
100
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
35-40
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) longitud., (+AT)
|
35
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+A)
|
215
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+AT)
|
200
|
|
|
|
|
|
|
|