产品详情
SA387GR22CL2现货/SA387GR22CL2价格/SA387GR22CL2切割加工
|
SA387Gr11CL2 |
10 |
2300 |
12000 |
|
SA387Gr11CL2 |
10 |
2300 |
12000 |
|
SA387GR22CL2 |
10 |
2300 |
12000 |
|
SA387GR22CL2 |
6 |
2200 |
12000 |
|
SA387GR22CL2 |
8 |
2000 |
8650 |
|
SA387GR22CL2 |
8 |
2300 |
10700 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
20 |
2200 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
16 |
2500 |
12000 |
|
SA387GR22CL2 |
16 |
2500 |
12000 |
四、SA387GR22CL2化学成分：
钢板的化学成分应符合表1的规定： Wt% 表1
成分
C
Si
Mn
P
S
Cr
V
Mo
Nb
熔炼分析
0.05~0.15
≤0.10
0.30~0.60
≤0.010
≤0.005
2.00~2.50
≤0.010
0.90~1.10
≤0.010
成品分析
0.04~0.15
≤0.10
0.25~0.63
≤0.010
≤0.005
1.95~2.60
≤0.010
0.87~1.13
≤0.010
Al
Ni
Cu
Ti
Sb*
Sn*
As*
[H]*
N*
O*
≤0.06
≤0.20
≤0.15
≤0.010
≤0.003
≤0.010
≤0.012
≤2PPm
≤80PPm
≤30PPm
≤0.06
≤0.25
≤0.15
≤0.010
≤0.003
≤0.010
≤0.012
≤2PPm
≤80PPm
≤30PPm
钢板厚度/mm
抗拉强度σb(Mpa)
屈服强度σs(Mpa)
伸长率A/%
温度/℃
冲击吸收能量KV2/J
180°弯曲试验 弯曲直径（b≥35mm）
6-150
520-680
≥310
≥19
20
≥34
d=3a
注： ⑴*分析结果只做记录，不作验收条件。
⑵熔炼分析按炉、成品分析按逐轧制张取样检验。
⑶回火脆化敏感性系数应满足以下要求： X=(10P+5Sb+4Sn+As)×10≤15PPm 式中元素以PPm含量代入，如0.01%应以100PPm代入。 J=(Si+Mn)(P+Sn)×10≤100 式中元素以其百分含量代入,如0.15%应以0.15代入。 P+Sn≤0.012%
五、SA387GR22CL2力学性能：
一、SA387GR22CL2简介：
适用范围 本技术条件适用于厚度≤150mm的临氢设备用SA387Gr22CL2(2 1/4Cr-1Mo)钢板的生产。
二、SA387GR22CL2执行标准：
美标：ASTM ASME钢板的尺寸、外形、重量及允许偏差应符合ASME SA387/SA387M标准之规定。
三、SA387GR22CL2交货状态：
钢板以正火（保证贝氏体组织≥90%的加速冷却 速度）+回火状态交货，正火温度不得超过968℃，回火温度不得低于720℃。 舞阳钢厂生产此种材质钢板